DOUBLE COMPONENT ELASTIC WATER INSULATION MORTAR

cift-komponentli-tam-elastik-su-izolasyon-harci

DESCRIPTION
Two component, semi flexible cementitious-liquid waterproofing mortar TS EN 14891-Liquid applied water impermeable products for use beneath ceramic tiling bonded with adhesive-requirements, test methods, evaluation of conformity, classification and designation CMP class

APPLICATION AREAS

Interior and exterior surfaces-horizontal and vertical waterproofing application
Waterproofing of wet areas for water inlet
Waterproofing of bathrooms, showers, balconies, terraces before laying ceramic tiles
Waterproofing of places to small deformation and water impermeability
Waterproofing of water tank except for drinking water tank

USAGE
Pour 10 liters liquid component into a suitable clean container. Then slowly add 20 kg powder component and mix with a low speed mixer to obtain a homogenous lump free mix. Mixing with max 400-600 rpm mixer is recommended. Allow to stand for 5 minutes to mature. After remixing, the paste is ready for application. Apply a thin layer with brush one direction then after first layer dry apply a second layer, to have a final thickness of approximately 2-3 mm. Expansion joints, joints between horizontal and vertical surfaces, areas with small cracks or places subject to stress it must be used Forcechem® Double Component Elastic Water Insulation Mortar Dilatation tape or interior tape for these joints. Unfavorable climatic conditions (high temperature, low humidity, wind etc.) can reduce this time to just a few minutes. Dispose mortars of which pot life is expired. Clean tools and hands with water, surfaces with a damp cloth. Protect the surface from direct sunlight, rain, freezing and wind for the first 24 hours after application.

MIXING RATIO

Forcechem® Double Component Elastic Water Insulation Mortar	Powder	Liquid
Mixing Ratio	20 kg	10 kg

CONSUMPTION
1.6 – 1,8 kg/m²/mm

TECHNICAL SPECIFICATION

Appearance	Grey
Content of Material	Powder Component: Cement, polymer and special additive Liquid Component: Styrene acrylic copolymer
Application Thickness	At least 2 mm – 4 mm
Mixing Time	Min 5 minutes
Water Impermeability (EN 14891)	≥ 3,0 bar (pozitif)
Adhesion Strength (EN 14891)	≥ 0.5 N/mm² (28 days normal condition)
	≥ 0.5 N/mm² (after heat storage condition)
	≥ 0.5 N/mm² (after water ageing condition)
	≥ 0.5 N/mm² (after froze-thaw cycle condition)
Crack Bridging Ability (EN 14891)	≥ 0.75 mm (standard condition)
Pot Life	1.5 hour
Waiting Time For Laying On	After 3 days
Open to Traffic	After 7 days
Temperature Resistance	-30 ⁰C / +80⁰C
Shelf Life	12 months under dry and suitable storage

Above informations at +21⁰C and %50 humidity